阀门及管路附件用氟塑料衬里性能表
阀门及管路附件用氟塑料衬里性能如下所示：
| 性能 | 名称 | 聚四氟乙烯 | 聚三氟氯乙烯 | 聚偏二氟乙烯 | 聚全氟乙炳烯 | 可溶性聚四氟乙烯 | 聚烯烃 | 聚乙烯 | 聚丙烯 | |
| 缩写 | PTEF | PCTFE | PVDF | FEP | PFA | PO | PE | PP | ||
| 代号 | F4 | F3 | F2 | F46 | *FA | – | – | – | ||
| 物理性能 | 比重 | g/cm3 | 2.1~2.2 | 2.1~2.2 | 1.76 | 2.1~2.2 | 2.1~2.2 | 0.92 | 0.92 | 0.92 |
| 吸水率 | % | 0.001~0.005 | ≤0.005 | 0.04 | ≤0.01 | ≤0.01 | 0.005 | 0.005 | 0.005 | |
| 成品收缩率 | % | 1~5 | 1~2.5 | 2.0 | 2~5 | 1~5 | 1~2 | 1~2 | 1~2 | |
| 热胀冷缩 | 10-5/K | 10~12 | 4.5~7.0 | 8.5~15.3 | 8.3~10.5 | 8.3~12 | – | – | – | |
| 脆化温度 | ℃ | -180~-195 | -80~-195 | -62 | -260 | -80~-195 | -40 | -40 | -20 | |
| 连续耐热 | ℃ | 260 | 120~190 | 150 | 204 | 260 | 100 | 100 | 110 | |
| 推荐使用温度 | ℃ | ≤180 | ≤120 | ≤100 | ≤150 | ≤180 | ≤85 | ≤85 | ≤100 | |
| 机械性能 | 硬度 | 邵氏 | D50~65 | D74~78 | D80 | (R45) | D50~65 | D40 | D40 | D40 |
| 摩擦系数 | – | 0.06 | 0.3~0.4 | 0.14~0.17 | 0.06~0.11 | 0.06~0.11 | – | – | – | |
| 拉伸强度 | MPa | 13.7~24.5 | 31.3~39.2 | 45~48.3 | 20.2~24.5 | 14~28 | ≥10 | 6.9~14 | 7.5~14 | |
| 弯曲强度 | MPa | 10.7~13.7 | 53.9~68.6 | – | – | 15~28 | – | – | – | |
| 压缩强度 | MPa | 111 | 80.3~50.9 | 68.6 | – | 111 | – | – | – | |
| 冲击强度 | kJ/m2 | 16 | 12.7~16.6 | 19.7 | 不断 | 1+ | 55 | 45 | 50 | |
| 极限延伸 | % | 250~350 | 30~190 | 30~300 | 250~270 | 300~500 | 480 | 300~600 | 600~700 | |
| 击穿电压 | KV/mm | 25~40 | 19.7 | 10.2 | 40 | 25~40 | – | – | – |
| 加工性能 | 模压成型 | 优 | 优 | 优 | 优 | 优 | 优 | 优 | 优 |
| 注射成型 | 优 | 优 | 优 | 优 | 优 | 优 | 优 | 优 | |
| 层压 | 优 | 优 | 优 | 优 | 优 | 优 | 优 | 优 | |
| 涂层 | 优 | 优 | 优 | 优 | 优 | 优 | 优 | 优 |
| 耐腐蚀性能 | 介质 | 浓度(%) | 温度(℃) | PTFE | PCTFE | PVDF | FEP | PFA | PO | PE | PP |
| 硫酸 | 10~98 | 常温~100 | A | A~B | A~B | A | A | 浓度≤50% 温度≤60℃ A | |||
| 硝酸 | 5~98 | 常温~100 | A | A | A | A | A | 浓度≤30% 温度≤60℃ A | |||
| 盐酸 | 10~38 | 常温~100 | A | A | A | A | A | 浓度≤38% 温度≤60℃ A~B | |||
| 醋酸 | 10~100 | 常温~100 | A | A~B | A~B | A | A | 浓度≤10% 温度≤60% A | |||
| 铬酸 | 50~100 | 常温~70 | A | A~B | A~B | A | A | 浓度≤30% 温度≤20℃ A | |||
| 磷酸 | 50~85 | 常温~100 | A~B | A | A | A~B | A~B | 浓度≤85% 温度≤20℃ A | |||
| 三氯甲烷 | 100 | 常温 | C | D | D | C | C | X X X | |||
| 硫酸铜 | 15 | 常温 | A | B | B | A | A | 浓度≤90% 温度≤80℃ A | |||
| 二乙醚 | 100 | 常温 | B | C | C | B | B | X X X | |||
| 醋酸乙醇 | 100 | 常温 | B | C | C | B | B | X X X | |||
| 汽油 | 100 | 常温 | A | A | A | A | A | X X X | |||
| 过氧化氢 | 3~30 | 常温 | A | A~B | A~B | A | A | 浓度≤30% 温度≤80℃ A | |||
| 王水 | – | 常温 | A | A | A | A | A | X X X | |||
| 硝基苯 | 100 | 常温 | A | B | B | A | A | X X X | |||
| 苛性钠 | 10~50 | 常温~100 | A | A~B | A~B | A | A | 浓度≤80% 温度≤60℃ A | |||
| 次氯酸钠 | – | 70 | A | A | A | A | A | 浓度≤80% 温度≤60℃ A~B | |||
| 氢氧酸 | 40~99 | -10~30 | A~B | B | B | A~B | A~B | 浓度≤80% 温度≤60℃ A~B | |||
| 发烟硫酸 | 20 | 常温 | A | B | B | A | A | X X X | |||
| 丙烯腈 | – | 常温 | B | C | C | B | B | – – – | |||
| 苯胺 | 100 | 常温 | B | B | B | B | B | 浓度≤60% 温度≤20℃ B | |||
| 苯 | 100 | 常温 | B | C | C | B | B | X X X | |||
| 醋酸丁酯 | 100 | 常温 | B | C | C | B | B | 浓度≤60% 温度≤20℃ B | |||
| 四氯化碳 | 试剂级 | 常温 | B | C | C | B | B | X X X | |||
注释：
1、阀门的推荐温度只是一个范围，仅供参考，阀门类的不同，随着DN的增大、使用温度要相应降低，需要合理选用温度。
2、ABCD表示耐腐蚀性能等级，分为优、良、合格、不合格。